The Evaluation of Brass and Low Carbon Steel Corrosion in Gabraun Water
Article Sidebar
-
Brass, Low Carbon Steel, Gabraun Water, Corrosion Rate, Pourbaix Diagrams, Langelier Saturation Index
Abstract
This work aimed to study the effect of Gabraun's water on the corrosion of brass and low carbon steel. The corrosion tests were carried out at room temperature. The test solution used was Gabraun water samples. From the results obtained, the weights of all the specimens after the immersion in Gabraun`s water were decreased. After the end of the experiments, the color of the Gabraun water samples that was used for the brass specimens was changed to a dark blue color, but for the low carbon steel, the color of the water did not change. During the corrosion tests period, the Gabraun water in the beakers decreased about 50 mL/week; this lack was substituted continuously by Gabraun water during the tests period. This addition of water increased the concentration of the salts of the Gabraun water samples. This increment played a role in the corrosion pprocess. he average corrosion rate for the low carbon steel is less than that of yellow copper specimens. The Langelier Saturation Index (LSI) showed that the Gabraun water sample was not a corrosive medium; also, it showed that all the Gabroun water samples, after testing, were not corrosive mediums. The Pourbaix diagrams for both copper and iron in the water at 25°C showed that both copper and iron are not corroded metals.
Full text article
References
[1]-www.startimes.com/?t=25903838(translated to English language on 27/3/2015)
[2]-Sidney H. Avner. Introduction to physical metallurgy copyright@ 1974,1964 by Mcgraw-Hill, Inc. ISBN 0-07-002499-5.
[3]-Herbert H. Uhlig. Corrosion and corrosion control. Second Edition. Cpyright©1963, 1971, byJohn Wiley & Sons, Inc. ISBN 0-471-89563-6.
[4]-N. D. Green. Corrosion-related chemistry and electrochemistry. Chapter 3, Basic corrosion course, NACE, Copyright 1970. USA
[5]-W. Qafsaoui, G. Mankowski, P. Leterrible and F. Dabosi, Proc. Inf. Symp. on Control of Copper and Copper alloysOxidation, July 6-8, 1992, Rotten, France MetaNurgie, (1992).
[6]-Sidney H. Avner "Introduction to physical Metallurgy" New York city community college city University of New York,1987.
[7]-Rakesh Dogra;Arvind Sharma "Advances in materials science "Beant college of Engineering and technology Gurdaspur (Punjab)1999.
[8]-MemonSamina, Abdulkarimand A.Venkatachalam. Corrosion Study of Iron and Copper Metals and Brass Alloy in Different Medium'' Department of Post Graduate Studies and Research in Chemistry Bhavan’s College, Andheri (W), Mumbai 400058, India Received 30 October 2010; Revised 4 March 2011; Accepted 12 April 2011 E-Journal of Chemistry2011, 8(S1), S344-S348
[9]-W. H. Rahmanto, Gunawan, and Rahmad Nuryanto. Corrosion rate of Copper and Iron in sea water based on resistance measurement. Electrochemical and Energetics Division of physical chemistry Laboratory. 2001
[10]-Howaida M. EL-Kashlan. Kinetics of Corrosion of Copper Metal in Presenceof Benzoic Acid.Asian Journal of Chemistry; Vol. 23, No. 12 (2011),5235-5246.
[11]-Jamal Abdulnasser, V. Rethinagiri and J. Abdulhakeem.Investigation of theinhibition of copper corrosion in nitric acid solutions by organic sulphide compound" Pelagia Research Library Advances in Applied Science Research, 2012, 3 (3):1749-1756 Trichy, India.
[12]-E.E. Foad El-Sherbini, Mustafa M. H. Khalil, Eman H. Ismail, and Soha S.Tobar.The Corrosion of Copper Metal in HCl Solutions and the Effect of Molybdate and Chromate" 16th International Conference on Aerospace Sciences & Aviation Technology. 2015, Military Technical College, Kobry Elkobbah, Cairo, Egypt.
[13]-www.researchgate.net/figure/pourbaix-diagram-of-copper(viewed on 2/12/2019)
[14]-https://www.nace.org/resources/general-resources/corrosion-basics/group-2/dezincification(viewed on 8/2/2020)
[15]-Jamal Choucri, Fedrica Zanotto, Vincenzo Grassi, Andrea Balbo, Mohamed Ebn Touhami, Ilyass Mansouri and Cecilia Monticelli. Corrosion Behavior of Different Brass alloys for Drinking Water Distribution system. Metals 2019, 9(6), 649. https://doi.org/10.3390/met9060649
[16]-Subir Paul, Anjan Pattanayak, and Sujit K. Guchhait. Corrosion Behavior of Carbon Steel in Synthetically Produced Oil Field Seawater" Department of Metallurgical and Material Engineering, Jadavpur University, Kolkata 700032, India Published 17December 2014 Academic Editor: Chi Tat Kwok.
[17]-1Engr Dr A.C Uzorh "Corrosion Properties of Plain Carbon Steels.The International Journal of Engineering and Science (IJES) Volume 2, Pages 18-24, 2013.): 2319 –180514.Nigeria.
[18]-Tadeusz Hryniewicz, Krzysztof Rokosz.Corrosion Behaviour of C45 Carbon Steel After Mechanical Surface Finishing" Technical University of Koszalin, Raclawicka 15-17, 75-620 Koszalin, METAL 2004.
[19]-Ismaeel Andijani and S. Turgoose.Studied on Corrosion of carbon steel in Deaerated Saline Solutions in Presence of Scale Inhibitor. Presented at the WSTA IV Gulf Conference, Bahrain, 13-18 February, 1999.
[20]-Sanusi KazeemOladele, Hussein Kehinde Okoro.Investigation of corrosion effect of mild steel on orange juice" African Journal of Biotechnology Vol. 10(16), pp. 3152-3156, 18 April, 2011 Academic Journals South Africa.
[21]-A.Ismail, N.H. Adan. Effect of Oxygen Concentration on Corrosion Rate of Carbon Steel in Seawater"American Journal of Engineering Research (AJER) Volume-03, Issue-01, pp-64-67 UniversitiTun Hussein Onn Malaysia (UTHM) Batu Pahat, Johor.
[22]-Mohammadreza Tavakkolizadeh, Hamid Saadatmanesh" Galvanic corrosion of carbon steel in Aggressive Environments" Journal of Composites for Construction /August 2001, P(200-2100).
[23]-A. A. M. Gebril and N. A. I. Ali. The effect of Gabraun water, Distilled water & Different Volumes of their mixture on corrosion rate of carbon steel. Journal of Sebha University (pure and applied sciences) vol. 16, No. 1, 2016.
[24]-A. A. M. Gebril. The effect of Gabraun`s water on corrosion of low carbon steel compared with other types of waterin south of Libya. Journal of Sebha University (pure and applied sciences). Vol. 15, No. 1, 2015
[25]-Corrosion Doctors, corrosion by water.(As viewed on 26/11/2019). http://www.corrosiondoctor.org/corrosion-by-water.htm
[26]-Bernard W. Lifka and Frank L. McGeary. (1970) Corrosion Testing. Nace Basic Corrosion Course. NACE. USA.
Authors
This work is licensed under a Creative Commons Attribution 4.0 International License.
In a brief statement, the rights relate to the publication and distribution of research published in the journal of the University of Sebha where authors who have published their articles in the journal of the university of Sebha should how they can use or distribute their articles. They reserve all their rights to the published works, such as (but not limited to) the following rights:
- Copyright and other property rights related to the article, such as patent rights.
- Research published in the journal of the University of Sebha and used in its future works, including lectures and books, the right to reproduce articles for their own purposes, and the right to self-archive their articles.
- The right to enter a separate article, or for a non-exclusive distribution of their article with an acknowledgment of its initial publication in the journal of Sebha University.
Privacy Statement The names and e-mail addresses entered on the Sabha University Journal site will be used for the aforementioned purposes only and for which they were used.